Effect of thin-layer conditions on stress-corrosion cracking of X70 steel in near neutral pH solution at cathodic polarization
DOI:
https://doi.org/10.62638/ZasMat1337Apstrakt
The priority task of modern underground main pipelines is to ensure the reliability of its operation, which largely depends on understanding the processes that occur on the surface of the pipes in the ground under conditions of cathodic protection. The purpose of this work is to study the features of stress-corrosion cracking (SCC) of X70 steel under conditions of thin-layer corrosion in near neutral pH environment. Potentiometry, voltammetry, massometry, electrolytic hydrogenation slow strain rate tests, scanning electronic microscopy were used. Differences in SCC mechanism of X70 steel at potentials of -0.950 V and -1.050 V in the investigated environments were experimentally determined. At -0.950 V, SCC of X70 steel in NS4 proceeds by anodic dissolution mechanism, and in the model soil environment - by mixed mechanism; at -1.050 V, SCC in the NS4 solution occurs by a mixed mechanism, and in a soil environment based on NS4 – by a hydrogen embrittlement mechanism. Obtained regularities are due to more significant embrittlement of the near-surface layer of the specimens in the model soil environment in thin layers under cathodic polarization, which leads to a change in SCC mechanism from plastic-brittle to completely brittle.
Ključne reči:
pipe steel, slow strain rate tests, potentiometry, voltammetry, stress-corrosion cracking, thin-layer corrosion, hydrogenationReference
I. S. Cole, D. J. C. S. Marney (2012) The science of pipe corrosion: A review of the literature on the corrosion of ferrous metals in soils, Corrosion science, 56, 5-16. https://doi.org/10.1016/j.corsci.2011.12.001
K. Yin, H. Liu, Y. F. Cheng (2018) Microbiologically influenced corrosion of X52 pipeline steel in thin layers of solution containing sulfate-reducing bacteria trapped under disbonded coating, Corrosion Science, 145, 271-282. https://doi.org/10.1016/j.corsci.2018.01.029
Wasim, M., Shoaib, S., Mubarak, N. M., Inamuddin, & Asiri, A. M. (2018). Factors influencing corrosion of metal pipes in soils. Environmental Chemistry Letters, 16, 861-879. https://doi.org/10.1007/s10311-018-0731-x
Suganya, S., & Jeyalakshmi, R. (2019) Corrosion of mild steel buried underground for 3 years in different soils of varying textures. Journal of Materials Engineering and Performance, 28, 863-875. https://doi.org/10.1007/s11665-019-3855-7
Ezuber, H. M., Alshater, A., Hossain, S. Z., El-Basir, A. (2021) Impact of soil characteristics and moisture content on the corrosion of underground steel pipelines, Arabian Journal for Science and Engineering, 46, 6177-6188. https://doi.org/10.1007/s13369-020-04887-8
Zhang, L., Li, X. G., & Du, C. W. (2009) Effect of environmental factors on electrochemical behavior of X70 pipeline steel in simulated soil solution. Journal of Iron and steel research, international, 16 (6), 52-57. https://doi.org/10.1016/S1006-706X(10)60027-1
Jiang, J., Wang, J., Lu, Y. H., & Hu, J. Z. (2009) Effect of length of gas/liquid/solid three-phase boundary zone on cathodic and corrosion behavior of metals, Electrochimica Acta, 54(5), 1426-1435. https://doi.org/10.1016/j.electacta.2008.09.017
Liu, H., Dai, Y., Cheng, Y. F. (2020) Corrosion of underground pipelines in clay soil with varied soil layer thicknesses and aerations, Arabian Journal of Chemistry, 13(2), 3601-3614. https://doi.org/10.1016/j.arabjc.2019.11.006
Wang, S., Du, C., Li, X., Liu, Z., Zhu, M., & Zhang, D. (2015). Field corrosion characterization of soil corrosion of X70 pipeline steel in a red clay soil. Progress in Natural science: Materials international, 25(3), 242-250. https://doi.org/10.1016/j.pnsc.2015.06.006
Song, Y., Jiang, G., Chen, Y., Zhao, P., & Tian, Y. (2017). Effects of chloride ions on corrosion of ductile iron and carbon steel in soil environments. Scientific reports, 7(1), 6865. https://doi.org/10.1038/s41598-017-07245-1
Bai, X., He, B., Han, P., Xie, R., Sun, F., Chen, Z., ... & Liu, X. (2022) Corrosion behavior and mechanism of X80 steel in silty soil under the combined effect of salt and temperature, RSC advances, 12(1), 129-147. https://doi.org/10.1039/D1RA08249C
Liu, Z. Y., Li, Q., Cui, Z. Y., Wu, W., Li, Z., Du, C. W., & Li, X. G. (2017) Field experiment of stress corrosion cracking behavior of high strength pipeline steels in typical soil environments, Construction and Building Materials, 148, 131-139. https://doi.org/10.1016/j.conbuildmat.2017.05.058
Fu, A. Q., Tang, X., & Cheng, Y. F. (2009) Characterization of corrosion of X70 pipeline steel in thin electrolyte layer under disbonded coating by scanning Kelvin probe, Corrosion Science, 51 (1), 186-190. https://doi.org/10.1016/j.corsci.2008.10.018
Yan, M., Wang, J., HAN, E. H., Sun, C., & Ke, W. (2014) Characteristics and evolution of thin layer electrolyte on pipeline steel under cathodic protection shielding disbonded coating, Acta Metall Sin, 50(9), 1137-1145. https://doi.org/10.11900/0412.1961.2014.00156
Gong, K., Wu, M., Xie, F., Liu, G., & Sun, D. (2020) Effect of dry/wet ratio and pH on the stress corrosion cracking behavior of rusted X100 steel in an alternating dry/wet environment, Construction and Building Materials, 260, 120478. https://doi.org/10.1016/j.conbuildmat.2020.120478
Zhiyong, L. I. U., Xiaogang, L. I., Zhang, Y., Cuiwei, D. U., & Guoli, Z. H. A. I. (2009) Relationship between electrochemical characteristics and SCC of X70 pipeline steel in an acidic soil simulated solution, Acta Metallurgica Sinica (English Letters), 22 (1), 58-64.
Hendi, R., Saifi, H., Belmokre, K., Ouadah, M., Smili, B., & Talhi, B. (2018) Effect of black clay soil moisture on the electrochemical behavior of API X70 pipeline steel, Materials Research Express, 5(3), 036523. https://doi.org/10.1088/2053-1591/aab40e
ISO 3183:2019 Petroleum and natural gas industries — Steel pipe for pipeline transportation systems
Antunes de Sena R, Napoleão Bastos І, Mendes Plat G. (2012) Theoretical and Experimental Aspects of the Corrosivity of Simulated Soil Solutions. International Scholarly Research Notices, Article ID 103715, 6 pages. https://downloads.hindawi.com/archive/2012/103715.pdf.
Nyrkova, L. I., Klymenko, A. V., Osadchuk, S. O., & Kovalenko, S. Y. (2024) Comparative investigation of electrolytic hydrogenation of pipe assortment steel under cathodic polarization. International Journal of Hydrogen Energy, 49, 1075-1087. https://doi.org/10.1016/j.ijhydene.2023.06.316.
Nyrkova, L. I., Klymenko, A. V., Goncharenko, L. V., Osadchuk, S. O., Kovalenko, S. Y., Kharchenko, Y. O., & Lavrenyuk, V. V. (2023) Influence of electrolytic hydrogenation on stress-corrosion cracking of X70 steel and pipes of long-term exploited main gas pipeline, Journal of hydrocarbon power engineering, 10(1), 15-24. https://doi.org/10.31471/2311-1399-2023-1(19)-15-24
Nyrkova, L. (2020) Stress-corrosion cracking of pipe steel under complex influence of factors, Engineering Failure Analysis, 116, 104757. https://doi.org/10.1016/j.engfailanal.2020.104757.
Nyrkova, L., Osadchuk, S. (2023) Stress-corrosion cracking of the steels of main gas pipeline: assessment and prevention. Kyiv, Naukova Dumka. 216 p. [in Ukrainian]. https://doi.org/10.15407/978-966-00-1845-7
NATIONAL STANDARD OF UKRAINE 4219-2003 STEEL PIPE MAINS. General requirements for corrosion protection. Kyiv, 2003. 86 p.